In the process of PTMS LITHIUM COBALT ACID MATERIAL MAGNETIC agitation before iron removal, when the stirring speed increases, the solid density can be increased, that is, the energy density can be increased, but it will cause a large number of nucleation caused by excessive saturation in the reaction. If the stirring rate reaches a certain value (adjust this value according to different proportions) the crystal growth rate is unchanged, then increasing the rate is undoubtedly too much wasted power cost.

PTMS magnetic separator

Influence of ammonium bicarbonate solution concentration: With the increase of ammonium bicarbonate concentration, the particles will increase significantly, the surface will become smoother, the particle distribution is better, and the sediment will gradually grow. The influence of PH value: when the PH value is in the range of 8--10 alkaline, the PH value rises, and the precipitation will continue to decrease after the saturation, when the PH value is 10--12, the precipitation increases with the increasing PH value, so it is very important to control the PH value, if the control PH value is 11, the precipitation product is single, the ball shape is good. Saving the cost of removing iron from PTMS LITHIUM COBALT ACID MATERIAL MAGNETIC.

what is magnetic separation in science?

The effect of reaction temperature: PTMS LITHIUM COBALT ACID MATERIAL MAGNETIC removal temperature has an appropriate value, the temperature exceeds the appropriate value, the bulk density will decrease, the temperature is less than the appropriate temperature, the reaction rate will be greatly improved.

Contact: DELLA

Mob: +86-13929907491

sales@powtechina.com