Metal element content to molar mass ratio of lithium 1:1.05 The precursor was mixed with lithium hydroxide, and then sintered at 800℃ and oxygen atmosphere to obtain high alkali material. The high-alkali material is finely broken into high-alkali material with an average particle size of 10μm. The high alkali MATERIAL and fine material are washed, pressed and dried, PTMS LITHIUM COBALT ACID MATERIAL MAGNETIC removal of iron to obtain washing material.
The ratio of metal element content to lithium molar mass 1:0.90 The precursor was mixed evenly with lithium hydroxide, and then sintered at 830℃ and oxygen atmosphere to obtain a low alkali feed. The low alkali material is finely broken into low alkali material with a particle size of 10μm. The washing material and low alkali material are put into the coating mixer according to the mass ratio of 2:1, and the coating agent boron oxide, which accounts for 0.5% of the mass of the whole mixed coating system, is put into the coating agent, and the coating material is obtained by mixed coating. The coating MATERIAL was sintered at 300℃ and oxygen atmosphere, and the PTMS LITHIUM COBALT ACID MATERIAL MAGNETIC was removed from the iron to obtain the high nickel ternary cathode material.
PTMS is the main PTMS magnetic separation equipment professional company, PTMS magnetic separation equipment for kaolin, potassium sodium feldspar, quartz sand removal of iron (Fe2O3). PTMS to provide customers with high quality PTMS magnetic separator, in addition to iron equipment and other products and services, the best choice of PTMS magnetic separator. PTMS develops, designs, and sells mining machinery, iron removal equipment, and dry magnetic separators.
Contact: DELLA
Mob: +86-13929907491