The speed of high-speed mixing is 40~50 revolution and 30~40 revolution. The medium speed is 20~30 revolution and 20~30 rotation; The speed of low speed mixing is revolution 10, rotation OHz. Use the instrument to drill out the LITHIUM ACID binary MATERIAL as the positive active substance, PTMS LITHIUM COBALT ACID MATERIAL MAGNETIC iron removal material high reaction voltage, good conductivity, stable structure will not collapse, low temperature discharge performance is good, very suitable for high power ion battery cathode material;
The conductive agent is a mixture of conductive graphite and carbon nanotubes. The carbon nanotubes are tubular hollow structures with large surface area and excellent conductive properties. Moreover, they are mixed with conductive graphite and N-methylated pyrolytic in advance and are evenly sealed and packaged. In the preparation process of positive slurry PTMS LITHIUM COBALT ACID MATERIAL MAGNETIC, the problems of material agglomeration and uneven dispersion do not occur, and the obtained slurry has good consistency.
The preparation method of PTMS LITHIUM COBALT ACID MATERIAL MAGNETIC is vacuum mixing. Adding appropriate amount of ethanol at the end of the mixing process can play a good role in defoaming, and there will be no white spots caused by bubbles during the coating process. Before the slurry coating, the 100-mesh screen can effectively remove particles and prevent the convex points caused by particles on the coating surface;
Contact: DELLA
Mob: +86-13929907491