The solvent Μ μ Inner Mongolia is 65% of the components according to the mass ratio LiCo: SP :PVDF = 95.7:2.3:2.ο of PTMS LITHIUM COBALT ACID MATERIAL MAGNETIC. The dispersion time of binder, conductive agent and active substance was 2 hours, 1 hour and 4 hours, and the final slurry viscosity was 5326Mpa · S.
The electrical performance of the prepared cylindrical battery was tested, and the production process of PTMS LITHIUM COBALT ACID MATERIAL MAGNETIC was drilled. The capacity retention rate of 1000 cycles was 97.23%, and the ratio of 1 was 93.23%. Comparison of energy density and internal resistance test results.
The LITHIUM batteries prepared by PTMS LITHIUM COBALT ACID MATERIAL MAGNETIC method have higher energy density and lower internal resistance than those prepared by conventional positive slurry production process.