PTMS LITHIUM COBALT ACID MATERIAL MAGNETIC was used for 12000Gs and 6000Gs magnetic intensity experiments. The number of each sample through the screen is 3 times. After the sample passes the screen for 3 times, the magnetic force is turned off, the magnetic material is recovered, the screen is removed, and the magnetic material attached to the screen is recovered.
Before iron removal, the iron content of the sample was 16mg. kg-i. PTMS LITHIUM COBALT ACID MATERIAL MAGNETIC After iron removal It can be seen from the table that after iron removal once under the magnetic strength of 12000Gs, the iron content of the product decreases from 16ppm to lppm, with a product rate of 93.6%. If the magnetic intensity is changed to 6000Gs, after removing iron twice, the iron content of the product is still Sppm, but the product rate is slightly higher, greater than 98%.
The indexes of finished ternary materials include total metal content (Ni+Co+Mn), metal content of each component, impurity content, pH value, specific surface area, particle size distribution, vibration-solid density, electrochemical performance, etc. PTMS LITHIUM COBALT ACID MATERIAL MAGNETIC after the removal of iron provides the control range and detection standards of each index, among which, the total metal content is generally selected by complexometric titration test, impurity elements and lithium elements are generally used by ICP test, all reach the standard.
Contact: DELLA
Mob: +86-13929907491